Capsules with opacifier

ABSTRACT

The present invention provides ingestible dosage form articles such as opaque capsules with reduced light transmittance.

TECHNICAL FIELD

The present disclosure relates to formulations for the production of opaque capsules or capsule shells and opaque capsules made therefrom. Said capsules shield the ingredient inside from light, while retaining good mechanical properties. The invention also relates to methods for making such capsules and the use thereof for delivery of the ingredients.

BACKGROUND OF THE INVENTION

Certain medicaments or other active ingredients such as nutraceutical etc. are sensitive to degradation by light and need to be stored in a light-shielded manner. Within capsules, the opacity of the capsule hence regulates the light-shielding. Typically in the prior art, titanium-dioxide (TiO₂) is used for creating opacity in the capsule shells.

Driven by the continuous search for new products, replacements of the well-known opacifier were sought.

There are many opacifiers, but due to their limited opacifying capacity, not all of them will give the capsules with good light blocking properties while maintaining the mechanical strength required for producing, processing and filling with active ingredient.

CaCO₃ is defined as one of many potential opacifiers, light blocking agents, light-shielding materials or pigments in a number of patents or patent applications such as: EP1580229A1, WO2011143347, WO2015174868A1, EP1502588A1, U.S. Pat. No. 3,784,684, EP1757275A1, JP2003300872A, US200244970A1, and US20100021535A1. However, none of these documents has documented experimental success with CaCO₃ in term of obtaining both an opacifying effect and retaining mechanical strength of capsules, when incorporating the CaCO₃ in the capsule formulation itself rather than applying it in some sort of coating on a capsule shell support. EP1574220A1 discloses the use of calcium lactate as an opacifier in HPMC-based capsules. Said calcium lactate however has a rather low refractive index and hence does not result in sufficient opacity. No information is given on the mechanical strength of such capsules.

Accordingly, it is an object of the present invention to provide capsules with light-shielding capacity, without the need of using TiO₂, and still remaining good mechanical properties.

SUMMARY

The present invention relates to capsule shell formulation design focusing on the selection of opacifiers that reduce the light transmittance of capsules while retaining the mechanical stability needed for producing, storing, processing, filling etc. of said capsules.

The inventors have established that calcium carbonate (CaCO₃), when present in a specific concentration range provided the best balance between good opacity and good mechanical properties, i.e. on the opacifying level and on the mechanical strength level for capsules.

This was unexpected, since numerous publications have been reporting on the potential use of calcium carbonate as opacifier, however without showing actual results on both opacity and mechanical strength, when the opacifier is mixed within the capsule forming formulation.

Having conducted extensive research on the matter, the inventors now put forward the following aspects of the invention:

Aspect 1. A capsule forming composition comprising:

-   -   a film forming agent selected from the group consisting of:         gelatin, polysaccharides, modified starches, cellulose         derivatives or synthetic polymers or a combination thereof; and     -   an opacifying agent in the form of calcium carbonate, preferably         precipitated calcium carbonate, in an amount of between 3 and 10         wt % based on dry weight of the capsule forming formulation.

Aspect 2. The capsule forming composition according to aspect 1, wherein said opacifying agent is present in an amount of between 4 and 8 wt %, more preferably of between 5 and 7 wt %, such as from 4.5 to 6.5 wt % based on dry weight of the capsule forming formulation.

Aspect 3. The capsule forming composition according to aspect 1 or 2, wherein said calcium carbonate has a substantially round or prismatic particle shape. In a particular embodiment, the calcium carbonate encompasses small round or prismatic uniform particles.

Aspect 4. The capsule forming composition according to any one of aspects 1 to 3, wherein said CaCO3 has a median particle size of between 0.2 and 2.0 μm or a. D4,3 particle size of about 10 μm or less.

The average particle size can be expressed as a “D50” (Dv50) median particle size of between 0.2 to 2 μm, such as between 0.5 and 1.5 μm, more preferably of between 0.3 to 1.2 μm, more preferably of between 0.4 to 1.1 μm, such as about 1 μm.

Alternatively, the particles can have a “D4,3” particle size of about 10 μm or less, more preferably of about 8 μm or less, such as about 6 μm or less, or about 4 μm or less, more particularly of between 1 and 10 μm, or between 1 and 8 μm, preferably of between 2 and 6 μm, more preferably of about 4 μm, e.g. between 3.5 and 4.5 μm.

In one embodiment, the particle size distribution, defined as particle size span, which is as low as possible. Preferably, said span is lower than 15, such as lower than 10, preferably below 8, more preferably below 6.

Aspect 5. The capsule forming composition according to any one of aspects 1 to 4, having a calcium carbonate concentration of about 10%, typically will have an opacity coefficient of 20% or higher. The capsule forming composition according to any one of aspects 1 to 4, having a calcium carbonate concentration of about 5%, typically will have an opacity coefficient of 15% or higher . . . . Alternatively, capsule forming composition according to any one of aspects 1 to 4 has a light transmittance at 650 nm of 35% or lower when the capsule comprises 10% calcium carbonate or a light transmittance at 650 nm of 55% or lower when the capsule comprises 5% calcium carbonate.

Aspect 6. The capsule forming composition according to any one of aspects 1 to 5, wherein said calcium carbonate is in the form of precipitated calcium carbonate.

Aspect 7. The capsule forming composition according to any one of aspects 1 to 6, wherein said film-forming agent is a cellulose based polymer such as methylcellulose, hydroxymethylcellulose, hydroxypropylcellulose, methylhydroxyethylcellulose, hydroxypropylmethylcellulose, hydroxypropylmethylcellulose phthalate, hydroxypropylmethylcellulose acetate succinate, carboxymethylethylcellulose or a combination thereof, preferably hydroxypropylmethylcellulose.

Aspect 8. The capsule forming composition according to any one of aspects 1 to 6, wherein said film-forming agent is a synthetic polymer such as polyvinyl alcohol, polyethylene glycol/oxide, polyvinyl acetate, poyacrylamide, poyvinylacetal diethylamino acetate, aminoalkylmethacrylate copolymer E, polyvinylpyrolidone, or a combination thereof.

Aspect 9. The capsule forming composition according to any one of aspects 1 to 6, wherein said film-forming agent is polypeptide-(protein-) based polymer such as gelatin, collagen, zein, casein, soy protein, or mung bean protein, whey protein, pea protein.

Aspect 10. The capsule forming composition according to any one of aspects 1 to 6, wherein said film-forming agent is a polysaccharide, preferably pullulan, starch, cellulose, or dextran.

Aspect 11. The capsule forming composition according to any one of aspects 1 to 6, wherein said film-forming agent is an acrylate and/or (meth)acrylate based polymer such as ethyl acrylate-methyl methacrylate copolymer, polyacrylic acid, or polymethyl methacrylate.

Aspect 12. The capsule forming composition according to any one of aspects 1 to 11, further comprising one or more additives such as: gelling agents, gelling aids, viscosity modifiers, de-foaming aids, plasticizers, lubricants, colorants, solvents, solvent aids, surfactants, dispersants, solubilizers, stabilizers, correctives, sweeteners, adsorbents, adherent's, antioxidants, antiseptics, preservatives, desiccants, flavors, perfumes, anti-oxidants, pH adjusters, binders, disintegrating agents, release-controlling agents.

Aspect 13. A capsule formed from the capsule forming composition according to any one of aspects 1 to 12.

Preferably, said capsule comprises:

-   -   a film forming agent selected from the group consisting of:         gelatin, polysaccharides, modified starches, cellulose         derivatives, or synthetic polymers; and     -   an opacifying agent in the form of calcium carbonate in an         amount of between 3 and 10 wt % based on dry weight of the         capsule forming composition, preferably in an amount of between         4 and 8 wt %, more preferably of between 5 and 7 wt %, such as         from 4.5 to 6.5 wt % based on dry weight of the capsule forming         composition.

In a preferred embodiment, when said capsule comprises HPMC as film-forming agent, the final capsule will comprise from 4 to 6 wt. % water based on the total capsule weight. In a further preferred embodiment, when said capsule comprises gelatin as film-forming agent the final capsule will comprise from 12 to 15 wt. % of water based on the total capsule weight. These concentrations are based on ambient temperature and humidity (25° C. (+/−2° C.) and RH of 30-50%).

Aspect 14. The capsule according to aspect 13, which is a hard shell capsule, preferably a gelatin, pullulan or HPMC based hard shell capsule.

Aspect 15. A method of producing a capsule with reduced light transmittance (also called opaque capsules), comprising providing the film-forming composition according to any one of claims 1 to 12, and forming capsules using a dip coating process.

Aspect 16. A method of preparing a film-forming composition according to any one of aspects 1 to 12, comprising the steps of:

a) preparing an aqueous dispersion of calcium carbonate opacifier, through mixing; b) preparing a film-forming formulation comprising one or more film-forming agent selected from the group of: gelatin, polysaccharides, modified starches, cellulose derivatives or synthetic polymers or a combination thereof; c) adding the aqueous dispersion of step a) to the solution of step b); and d) mixing the resulting dispersion of step c), thereby obtaining the film forming composition, comprising between 3 and 10 wt %, preferably of between 4 and 8 wt %, more preferably of between 5 and 7 wt %, such as from 4.5 to 6.5 wt % CaCO3 based on final dry weight of the film-forming composition. In one embodiment, said film-forming composition comprises 15-25 wt % HPMC such as 20.5 wt % HPMC; or 25-35 wt %, such as about 31 wt % gelatin based on total dry weight of final capsule forming formulation.

Aspect 17. The method according to aspect 16, wherein step c) is performed in two steps: c1) adding a part of the film-forming formulation of step b) to the dispersion of step a) to form a slurry and c2), adding said slurry to the remaining film forming formulation. Preferably, said slurry is formed using high shear mixing such as mixing at a speed of at least 10000 rpm, such as e.g. 12000 rpm or more for at least 2 minutes.

Aspect 18. The method according to aspect 16 or 17, wherein said mixing in step a) encompasses high shear mixing, such as mixing at a speed of at least 15000 rpm, preferably at least 20000 rpm for at least 4 minutes.

Aspect 19. The method according to any one of aspect 16 to 18, wherein the film-forming agent comprises gelatin, pullulan, HPMCAS or HPMC.

Additionally, the film-forming solution further comprises one or more additives such as: gelling agents, gelling aids, viscosity modifiers, de-foaming aids, plasticizers, lubricants, colorants, solvents, solvent aids, surfactants, dispersants, solubilizers, stabilizers, correctives, sweeteners, adsorbents, adherent's, antioxidants, antiseptics, preservatives, desiccants, flavors, perfumes, anti-oxidants, pH adjusters, binders, disintegrating agents, release-controlling agents.

Aspect 20. The method according to any one of aspects 16 to 19, wherein the opacifier is present in an amount of between 4 and 8 wt %, more preferably of between 5 and 7 wt % based on final dry weight of the film-forming composition.

Aspect 21. A method of making capsules comprising the steps of:

a) preparing a film forming composition according to the method of any one of aspects 16 to 20 and b) producing a capsule by means of dip molding. Typically, such a dip molding method comprises the steps of: dipping a mold pin in the film-forming composition at an adequate temperature to allow film-forming thereof on said dipping pin; (air-)drying said film on the dipping pin; and removing the film-formed capsule half from said dipping pin.

Aspect 22. The capsule according to aspect 13 or 14, or the capsule obtained by the method of aspect 21, wherein:

-   -   when the capsule is an HPMC capsule having a calcium carbonate         concentration of about 5 or 10%, it typically will have an         opacity coefficient of 20% or higher. An HPMC capsule with 5%         CaCO₃ will typically have a light transmittance at 650 nm of 35%         or lower, while an HPMC capsule having about 10% CaCO₃ typically         will have a light transmittance at 650 nm of 10% or lower.     -   when the capsule is an HGC capsule having a calcium carbonate         concentration of about 5 or 10%, it typically will have an         opacity coefficient of 17% or higher. An HGC capsule with 10%         CaCO₃ will typically have a light transmittance at 650 nm of 30%         or lower, while an HGC capsule having about 5% CaCO₃ typically         will have a light transmittance at 650 nm of 55% or lower.

These values are determined on the average capsule wall thickness of standard capsules, i.e. of about 100 μm.

Aspect 23. The capsule according to aspect 22, filled with a filling formulation comprising an active ingredient such as a nutrient or a medicament.

Aspect 24. The capsule according to aspect 23, wherein the active ingredient is present in an amount ranging from about 0.05 wt % to about 100 wt % based on the total dry weight of said filling formulation. Typically, the active ingredient can present in an amount ranging from about 0.5 wt % to about 90 wt % based on the total dry weight of said filling formulation, preferably from about 1 wt % to about 50 wt %, more preferably from about 5 wt % to about 30 wt % based on the total weight of said filling formulation

Aspect 25. The capsule according to any of aspects 23 or 24, wherein the active ingredient is an active pharmaceutical ingredient, nutritional supplement, nutraceutical, vitamin, mineral, cosmetic, health food, preferably a light unstable active ingredient.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1: SEM images of different types of CaCO₃ particles: A) precipitated CaCO₃ presenting small uniform round/prismatic particles; B) encapsulated CaCO₃ showing agglomerated granules forming large particles (up to 100 μm).

DETAILED DESCRIPTION OF THE INVENTION

Development of dosage forms such as capsules, with limited light transmittance, e.g. to protect light-unstable active ingredients is often a balancing act between opacity and mechanical strength and stability of the capsule shell.

The inventors have now identified the concentration range and type of calcium carbonate that provides a good balance to achieve both good opacifying effect and mechanical strength

It is to be understood that the terminology used herein is not intended to be limiting, since the scope of the present invention will be limited only by the appended claims.

As used herein, the singular forms “a”, “an”, and “the” include both singular and plural referents unless the context clearly dictates otherwise.

The terms “comprising”, “comprises” and “comprised of” as used herein are synonymous with “including”, “includes” or “containing”, “contains”, and are inclusive or open-ended and do not exclude additional, non-recited members, elements or method steps. The terms also encompass “consisting of” and “consisting essentially of”.

The recitation of numerical ranges by endpoints includes all numbers and fractions subsumed within the respective ranges, as well as the recited endpoints.

The term “about” as used herein when referring to a measurable value such as a parameter, an amount, a temporal duration, and the like, is meant to encompass variations of and from the specified value, in particular variations of +/−10% or less, preferably +/−5% or less, more preferably +/−1% or less, and still more preferably +/−0.1% or less of and from the specified value, insofar such variations are appropriate to perform in the disclosed invention. It is to be understood that the value to which the modifier “about” refers is itself also specifically, and preferably, disclosed.

Whereas the term “one or more”, such as one or more members of a group of members, is clear per se, by means of further exemplification, the term encompasses inter alia a reference to any of said members, or to any two or more of said members, such as, e.g., any 3, 4, 25, 26 or 7 etc. of said members, and up to all said members.

The expression “low light transmittance” when used in combination with capsules or capsule formulations refers to capsules or capsule formulations that allow limited light transmittance and hence are to some extent capable of blocking light (e.g. natural or artificial) from entering into the cavity of the capsule body comprising the active ingredient. For a capsule comprising 10 wt. % precipitated CaCO₃ in its shell, typically an opacity coefficient of about 20% or more is envisaged, such as 25% or more, or 35% or more. Alternatively, the light transmittance coefficient can be indicated and implies the amount of light that is allowed to enter through the capsule shell. Typically a transmittance at 650 nm of below 35% is envisaged, preferably of below 25%, such as about 20% or less, or about 10% or less. For a capsule comprising 5 wt. % precipitated CaCO₃ in its shell, typically an opacity coefficient of about 15% or more is envisaged. Alternatively, the light transmittance coefficient can be indicated and implies the amount of light that is allowed to enter through the capsule shell. Typically a transmittance at 650 nm of below 55% is envisaged.

The opacity and transmittance of the capsules of the invention depend on the type of film forming polymer used and on the concentration of CaCO₃ used. As an exemplary guidance:

when the capsule is an HPMC capsule having a calcium carbonate concentration of about 5 or 10%, it typically will have an opacity coefficient of 20% or higher. An HPMC capsule with 5% CaCO₃ will typically have a light transmittance at 650 nm of 35% or lower, while an HPMC capsule having about 10% CaCO₃ typically will have a light transmittance at 650 nm of 10% or lower; when the capsule is an HGC capsule having a calcium carbonate concentration of about 5 or 10%, it typically will have an opacity coefficient of 17% or higher. An HGC capsule with 10% CaCO₃ will typically have a light transmittance at 650 nm of 30% or lower, while an HGC capsule having about 5% CaCO₃ typically will have a light transmittance at 650 nm of 55% or lower; these values being determined on the average capsule wall thickness of standard capsules, i.e. of about 100 μm. There are several methods for measuring particle size and particle size distribution. Some of them are based on light, other on ultrasound, or electric field, or gravity, or centrifugation.

In all methods the size is an indirect measure, obtained by a model that transforms, in abstract way, the real particle shape into a simple and standardized shape, like a sphere (the most usual) or a cuboid (when minimum bounding box is used), where the size parameter (ex. diameter of sphere) makes sense. Exception is the mathematical morphology approach, where no shape hypothesis is necessary.

Definition of the particle size for an ensemble (collection) of particles presents another problem. Real systems are practically always polydisperse, which means that the particles in an ensemble have different sizes. The notion of particle size distribution reflects this polydispersity. There is often a need for a certain average particle size for the ensemble of particles.

The term “D50 average particle size”, or “Dv50”, or volume basis median particle size indicates that in the particle mixture, the diameter of 50% (on the total mass) of the particles is smaller than, and the diameter of the other 50% (on the total mass) of the particles is larger than the indicated D50 average size. Typical measurement techniques are sieve analysis, direct imaging and laser diffraction known in the art.

The term “D4,3 average diameter size” or mean diameter over volume (also called the DeBroukere mean, following the conventions from ref. 2, ASTM E 799), is the mean particle size based on the volume distribution and implies that the volume mean is used to define the central point of size distribution, although the median is more frequently used than the mean when using this technique. The values for D[4,3] are strongly impacted by the presence of aggregates which are not easily broken during measurement causing strong variation in measured particles size in the larger particles range. The equation is as follows:

${D\left\lbrack {4,3} \right\rbrack} = \frac{\sum\limits_{1}^{n}D_{i^{v}i}^{4}}{\sum\limits_{1}^{n}D_{i^{v}i}^{3}}$

The term “particle size distribution”, reflects the width or breadth of the distribution or particle sizes. Several calculations are used to describe the width of distribution but the most common calculations are standard deviation and variance.

The term “particle size span”, indicates the broadness of particle size distribution and follows the equation: Span=(Dv0.9−Dv0.1)/Dv0.5, wherein Dv0.9 (D90), Dv0.1 (D10) and Dv0.5 (D50) represent the size at which respectively 90%, 10% and 50% of the particles are below said size, as e.g. measured by laser diffraction.

The term “high shear mixing” encompasses any type of high shear mixing at a speed of at least 15000 rpm, preferably at least 20000 rpm for at least 4 minutes. As a non-limiting example one can use the IKA Ultra Turraxx T25 mixer. The concentration of the dispersion is preferably at least 15 wt %, preferably above 20 wt %.

All documents cited in the present specification are hereby incorporated by reference in their entirety.

Unless otherwise specified, all terms used in disclosing the invention, including technical and scientific terms, have the meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. By means of further guidance, term definitions may be included to better appreciate the teaching of the present invention.

The film-forming agent referred to herein can by any type of film-forming agent. Particularly envisaged film-forming agents are gelatin, polysaccharides, modified starches, or synthetic polymers. Non-limiting examples thereof include generally known agents, for example: cellulose based polymers such as methyl cellulose, ethyl cellulose, methylhydroxyethyl cellulose, hydroxypropyl cellulose, hydroxypropylmethyl cellulose, hydroxypropylmethylcellulose phthalate, hydroxypropylmethylcellulose acetate succinate, carboxymethylethylcellulose, and the like, polysaccharides such as pullulan, carrageenan, gellan, alginates, and the like; or gelatin; synthetic polymers such as polyvinyl alcohol, poyvinylacetal diethylamino acetate, aminoalkylmethacrylate copolymer E (Eudragit-E-Rohm Pharma Co. Ltd.), poyvinylpyrolidone, and the like; (meth)acrylate based polymers such as ethyl acrylate-methyl methacrylate copolymer suspensions (Eudragit N E (commercial name), Rohm Pharma Co. Ltd.), and the like; acrylate based polymers such as methacrylate copolymer L (Eudragit L-Rohm Phamia Co. Ltd.), methacrylate copolymer LD (Eudragit L-30D55-Rohm Pharma Co. Ltd.), and the like; as well as any combination thereof.

Gelatin, pullulan and cellulose based polymers are preferred. Of said cellulose based polymers, methylhydroxyethylcellulose, hydroxypropylcellulose, hydroxypropylmethylcellulose, and hydroxypropylmethylcellulose acetate succinate are more preferably used.

In addition to the film-forming agent(s), other additives can be added such as plasticizers, colorants, solvents, solvent aids, dispersants, solubilizers, stabilizers, correctives, sweeteners, adsorbents, absorbents, adherents, antioxidants, antiseptics, preservatives, desiccants, flavors, perfumes, pH adjusters, binders, lubricants, humectants, disintegrating agents, and/or release-controlling agents known in the art.

Adding additives such as dispersants (e.g. (iota-)carrageenan, sodium lauryl sulfate, sorbitan, or lecithin) can be beneficial.

When hard capsule shells are envisaged, said capsule shells may optionally further include other minor components conventionally used in capsules or that are used in the aqueous composition for dipping and that remain as part of the finished capsule. Examples of such materials include surfactants, de-foaming aids, anti-oxidants, viscosity modifiers, gelling agents, gelling aids, lubricants and plasticizers.

So called “setting systems” comprising gelling agents and/or gelling aids are conventionally relied upon in the manufacture of hard capsule shells by non-thermogelling dip-molding processes to confer an appropriate setting ability with cooling to film-forming polymers (like pullulan, HPMC or starch derivatives) that in these conditions have per se poor gelling properties. The setting system makes the aqueous composition to set on the dipped pins, thus enabling capsules production and assuring a uniform capsule shell thickness.

Such gelling agents and aids are well known in the art. Depending on the film-forming polymers to be used in the capsule shell manufacturing we refer to for example to U.S. Pat. No. 5,264,223 and EP714656 (discussing HPMC capsules), EP1117736 (discussing starch derivatives capsules); WO2005105051 and EP1072633 (discussing pullulan capsules).

In one embodiment, the setting system of the invention comprises one or more gelling agents. In one embodiment, the setting system of the invention comprises one or more gelling agents and one or more gelling aids, also known as co-gelling agents.

In one embodiment, the one or more gelling agents are selected from the group consisting of alginates, agar gum, guar gum, locust bean gum (carob), carrageenan (preferably kappa, lambda, and/or iota), tara gum, arabic gum, ghatti gum, khaya grandifolia gum, tragacanth gum, karaya gum, pectin, arabian (araban), xanthan, low and high acyl gellan gum, starch, konjac mannan, galactomannan, funoran, acetan, welan, rhamsan, furcelleran, succinogycan, sclerogycan, schizophyllan, tamarind gum, curdlan, dextran and mixtures thereof. Preferably, the one or more gelling agents are selected from the group consisting of carrageenans (preferably kappa and/or iota, more preferably kappa-carrageenans), gellan gum and mixtures thereof. In one embodiment, the one or more gelling agents comprise, preferably consist of carrageenans (preferably kappa and/or iota, more preferably kappa-carrageenans). In one embodiment, the one or more gelling agents comprise, preferably consist of gellan gum.

In one embodiment, the one or more gelling agents comprise a combination of two or more of the agents listed above. In one embodiment, the one or more gelling agents comprise, preferably consist of a combination of xanthan and locust bean gum. In one embodiment, the one or more gelling agents comprise, preferably consist of a combination of xanthan with konjac mannan.

In one embodiment, the one or more gelling aids (also known as co-gelling agents) are cations. In one embodiment, the one or more gelling aids are selected from the group consisting of: K, U, Na⁺, NH₄ ⁺, Ca²⁺, Mg²⁺ and mixtures thereof. Preferably, the one or more gelling aids are selected from the group consisting of: K⁺, NH₄ ⁺, Ca²⁺ and mixtures thereof. The cations can be added to the setting system in the form of a pharmaceutically or food acceptable water soluble salt (e.g. chloride, acetate, citrate or phosphate).

In one embodiment, the setting system of the invention comprises one or more gelling agents selected from the group consisting of: carrageenans (preferably kappa and/or iota, more preferably at least kappa-carrageenans), gellan and mixtures thereof; and one or more pharmaceutically or food acceptable water soluble salts of K⁺, NH₄ ⁺, Ca²⁺ and mixtures thereof.

In one embodiment, the aqueous composition of the invention contains one or more gelling agents as defined above in an amount suitable to obtain a hard capsule shell as defined below containing between about 0.01 and 3.0%, by weight, preferably between about 0.03 and 1.0%, by weight, preferably between about 0.1% and 0.5% by weight of such gelling agent(s) over the weight of the shell. Exemplary suitable gelling agents' amounts are readily available to a skilled person in the field of hard capsules manufacturing. For example, it is commonly accepted that hard capsule shells containing a “target” amount of gelling agents falling within the ranges identified above can be obtained via a dip-molding process by using aqueous compositions containing about ¼ (i.e. 25%) of that target amount (expressed as % by weight over the weight of the composition).

In one embodiment, the aqueous composition of the invention contains one or more gelling aids as defined above in an amount suitable to obtain a hard capsule shell as defined below containing about less than 3%, preferably about less than 2.0%, more preferably between about 0.5% to 2.0%, even more preferably between about 1.0% and 2.0% by weight of such one or more gelling aids over the weight of the shell. In case the gelling aids are cations, the above ranges are expressed as weight of the pharmaceutically or food acceptable water soluble salts containing the cation(s) over the weight of the shell. Exemplary suitable gelling aids amounts are readily available to a skilled person in the field of hard capsules manufacturing. For example, it is commonly accepted that when water is about 75% by weight over the weight of the aqueous composition, hard capsule shells containing a “target” amount of gelling aids can be obtained via a dip-molding process by using aqueous compositions containing about ¼ (i.e. 25%) of that target amount (expressed as % by weight over the weight of the composition).

The hard capsule shells can also contain residual water. Typically such shells comprise, for example, less than 25 wt %, preferably less than 20 wt %, more preferably from 0 wt % to 14 wt %, even more preferably from greater than 1 wt % to less than 10 wt %, and more preferably from 2 wt % to 7 wt % water by weight.

Although any active ingredient selected from active pharmaceutical ingredients, nutritional supplements, nutraceuticals, vitamins, minerals, cosmetics, health foods, or the like can be encapsulated in the capsule formulation of the present invention, light-unstable or light-sensitive ingredients are particularly suited. Non-limiting light-unstable medicaments that can be filled in the capsules to obtain effective light shielding are: dihydropyridine derivatives (e.g., nifedipine), antiviral HIV protease inhibitors (e.g., Ritonavir, Saquinavir), therapeutic agents for hyperlipidemia (e.g., clofibrate), iodine compounds (e.g., sodium iopodate, sodium iodide), polyunsaturated fatty acid derivatives (e.g., ethyl eicosapentaenoic acid (EPA), docosahexaenoic acid (DHA)), carotenoids (e.g., lycopene, bixin, β-carotene, xanthophyll, lutein), ubiquinones (coenzyme Q)(e.g., ubidecarenone used as a metabolizable cardiac stimulant), various vitamin derivatives, as well as indomethacin, colchicine, diazepam, syrosingopine, norethisterone, piretanide, propericyazine, perphenazine, mequitazine, medazepam, menatetrenone, indenolol hydrochloride, reserpine, sofalcone, bromocriptine mesilate, bufetolol hydrochloride and oxprenolol hydrochloride when they are filled into the capsule formulation of the present invention. Among vitamin derivatives, fat-soluble ones are preferred for use. Examples include vitamin A derivatives (e.g., tretinoin, liver oil, retinol palmitate), vitamin A analogs (e.g., etretinate), vitamin D derivatives, vitamin E derivatives (e.g., tocopherol nicotinate, tocopherol acetate, tocopherol calcium succinate), and vitamin K derivatives (e.g., phytonadione (vitamin K1), menaquinone (vitamin K2), menadione (vitamin K3), menatetrenone, phytonadione).

A medicament as an active ingredient can be filled into the capsules of the present invention, either alone or in combination with any base or carrier, additive, or excipient. Any type of base or carrier, either fat-soluble or water-soluble, can be used as long as it does not impair the medicament's activity and does not affect various physical properties of the capsule shell, such as strength, gas permeability, and disintegration or dissolution profiles. Likewise, the base per se may be in a liquid or solid state at normal temperature as long as it can be filled into capsules with the help of heating or dilution with other solvents, etc. Examples of such a base include vegetable oils (e.g., soybean oil, sesame oil, cottonseed oil, olive oil), fatty acid glycerides (e.g., medium chain triglycerides), propylene glycol, propylene glycol fatty add esters, polyethylene glycol, polyvinylpyrrolidone, triacetin, liquid paraffin, polyoxyethylene sorbitan fatty acid esters, sucrose fatty acid esters, ethanol and purified water, which may be used alone or in combination. Bases preferred for dissolving fat-soluble medicaments such as vitamins A, D, E and K are vegetable oils or fatty acid glycerides, with medium chain triglycerides being particularly preferred. In the case of using a water-soluble base, it is preferable to provide a protection layer between the shell layer and the medicament layer or a crystallization inhibitor in consideration of influences on the capsule shell.

A medicament to be filled into the capsule shell of the present invention is preferably exemplified by, but not limited to, those in a liquid form or those dissolved, suspended or emulsified in such a base as listed above. The medicament may also be in a solid form (e.g., powders, granules) or in a semi-solid form (e.g., creams or gels).

The invention hence provides for a capsule formulation for forming capsules with reduced light transmittance (also called opaque capsules) comprising:

-   -   a film forming agent as defined herein; and     -   an opacifying agent in the form of calcium carbonate in an         amount of between 3 and 10 wt % based on dry weight of the         capsule forming formulation. Preferably, said CaCO₃ is present         in an amount of between 4 and 8% based on dry weight of the         final capsule forming formulation, more preferably in an amount         of between 4.5 and 6.5 wt % based on dry weight of the final         capsule forming formulation.

As will become clear from the examples section, the amount and particle size of the calcium carbonate as well as the type of CaCO₃ influences the balance between opacity and mechanical strength of the films and capsules envisaged herein.

The inventors have found that a median particle size (Dv50) of between 0.2 and 2.0 μm and/or a D4,3 particle size of about 10 or less is particularly advantageous for forming such films and capsules.

The average particle size can be expressed as a “D50” (Dv50) median particle size of between 0.2 to 2 μm, such as between 0.5 and 1.5 μm, more preferably of between 0.3 to 1.2 μm, more preferably of between 0.4 to 1.1 μm, such as about 1 μm.

Alternatively, the particles can have a “D4,3” particle size of about 10 μm or less, more preferably of about 8 μm or less, such as about 6 μm or less, or about 4 μm or less, more particularly of between 1 and 10 μm, or between 1 and 8 μm, preferably of between 2 and 6 μm, more preferably of about 4 μm, e.g. between 3.5 and 4.5 μm.

Preferably, said calcium carbonate has a substantially round/prismatic particle shape. In a particular embodiment, the calcium carbonate encompasses small uniform round or prismatic particles

Typically, the particle size span of the CaCO₃ particles as defined above is as low as possible. Preferably, said span is below 10, preferably below 8, more preferably below 6.

In a preferred embodiment, the CaCO₃ is precipitated, i.e. is prepared from calcium oxide (CaO-lime), whereto water is added to give calcium hydroxide. Subsequently carbon dioxide is passed through this solution to precipitate the desired calcium carbonate, in the industry as precipitated calcium carbonate (PCC). PCC is available in numerous crystal morphologies and sizes, which can be tailored to optimize performance in a specific application. The calcium oxide used as starting material for the precipitation process can be obtained through the milk of lime process, which encompasses crushing of high purity calcium carbonate rock into small particles or powder suitable for processing, heating the latter to about 1000° C., thereby taking the calcium carbonate apart into calcium oxide (CaO) and carbon dioxide (CO₂) which can be captured and reused in the precipitation process above.

In a preferred embodiment, said PCC has a median particle size of between 0.2 and 2.0 μm or a. D4,3 particle size of about 10 μm or less. Alternatively, the average particle size of PCC can be expressed as a “D50” (Dv50) median particle size of between 0.2 to 2 μm, such as between 0.5 and 1.5 μm, more preferably of between 0.3 to 1.2 μm, more preferably of between 0.4 to 1.1 μm, such as about 1 μm.

The invention hence provides for a method of preparing a film-forming composition with opacifying capacities comprising the steps of:

a) preparing an aqueous dispersion of calcium carbonate opacifier through mixing; b) preparing a film-forming formulation comprising one or more film-forming agent selected from the group of: gelatin, polysaccharides, modified starches, (meth)acrylate based polymers, or synthetic polymers or a combination thereof; c) adding the aqueous dispersion of step a) to the solution of step b); and d) mixing the resulting dispersion of step c), thereby obtaining the film forming composition, comprising between 3 and 10 wt %, preferably of between 4 and 8 wt %, more preferably of between 5 and 7 wt %, such as from 4.5 to 6.5 wt % CaCO3 based on final dry weight of the film-forming composition. In one embodiment, said film-forming composition comprises 15-25 wt % HPMC such as 20.5 wt % HPMC; or 25-35 wt %, such as about 31 wt % gelatin based on total dry weight of final capsule forming formulation.

In one embodiment, said film-forming composition comprises 15-25 wt % HPMC such as 20.5 wt % HPMC; or 25-35 wt %, such as about 31 wt % gelatin based on total dry weight of final capsule forming formulation.

In one embodiment, step c) is performed in two steps: c1) adding a part of the film-forming formulation of step b) to the dispersion of step a) to form a slurry and c2), adding said slurry to the remaining film forming formulation.

Preferably, said slurry is formed using high shear mixing such as mixing at a speed of at least 10000 rpm, such as e.g. 12000 rpm or more for at least 2 minutes.

In one embodiment, said mixing in step a) encompasses high shear mixing, such as mixing at a speed of at least 15000 rpm, preferably at least 20000 rpm for at least 4 minutes.

Without wanting to be bound to any theory, the high shear mixing can result in a better dispersion of the CaCO₃ in the film-forming composition, leading to increased mechanical strength.

In one embodiment, the opacifier is present in an amount of between 3-10 wt %, such as between 4 and 8 wt %, more preferably of between 5 and 7 wt % based on final dry weight of the film-forming composition.

The invention also provides in a method of making capsules comprising the steps of:

a) preparing a film forming composition as defined herein and b) producing a capsule e.g. by the conventional processes like extrusion moulding, injection moulding, casting or dip moulding. Typically, such a dip molding method comprises the steps of: dipping a mold pin in the film-forming composition at an adequate temperature to allow film-forming thereof on said dipping pin; ((hot)-air-)drying of the said film on the dipping pin; and removing the film-formed capsule half from said dipping pin.

The capsules obtained through the methods as described herein typically will have an opacity coefficient of about 20% or higher and/or a light transmittance at 650 nm of 35% or lower when e.g. a concentration of 10% w/w of precipitated calcium carbonate is used. When using a lower concentration of calcium carbonate such as about 5%, an opacity coefficient of about 17% or higher and/or a light transmittance at 650 nm of 55% or lower is reached. Said ranges are based on a capsule wall thickness of approximately 100 μm (e.g. from 90 μm to 110 μm) as is standardly used for commercial capsules.

Such capsules can of course be used for delivery of any type of ingredient but are particularly suitable for active ingredients that have limited light-stability. Examples of active ingredients can be active pharmaceutical ingredients, nutritional supplements, nutraceuticals, vitamins, minerals, cosmetics, health foods, or the like. Such an ingredient can be present in an amount of between 0.05 wt % to up to 100 wt %. Typically, the active ingredient can present in an amount ranging from about 0.5 wt % to about 90 wt % based on the total dry weight of said filling formulation, preferably from about 1 wt % to about 50 wt %, more preferably from about 5 wt % to about 30 wt % based on the total weight of said filling formulation.

In one embodiment, the capsules in which the opacifier is used are: HPMC-based capsules such as plant based capsules called VegiCaps, or Vcaps® as described in U.S. Pat. No. 6,517,865; Vcaps®Pus as described in U.S. Pat. No. 9,655,860; Pullulan-based capsules such as those described in U.S. Pat. No. 6,887,307; or enteric capsules such as Vcaps® Enteric, described in WO2018/017799A1 and WO2013164121, the contents of which is hereby incorporated by reference. The preferred methods for producing such methods are also disclosed in said patents and hereby incorporated by reference.

The present invention is further illustrated in the following non-limiting examples.

EXAMPLES Materials and Methods

Mechanical Strength Testing of Films

Film mechanical properties were determined by tensile tests performed according to ASTM D882-02 (using Instron 5965) on the samples that were stored at 22° C. and 50% RH and 23% RH. Films were stored at these conditions for 7 days. For most tensile testing of materials, you will notice that in the initial portion of the test, the relationship between the applied force, or load, and the elongation the specimen exhibits is linear. In this linear region, the line obeys the relationship defined as “Hooke's Law” where the ratio of stress (a) to strain (E) is a constant, or according to Hooke's law:

$\frac{\sigma}{ɛ} = E$

“E” is the slope of the line in this region where stress (a) is proportional to strain (E) and is called the “Modulus of Elasticity” or “Young's Modulus”.

Mechanical Strength of Capsules

Test capsules are prepared as outlined below from the different film-forming compositions using conventional dip mold technology, wherein size 0 capsules are produced, having a capsule side wall thickness of about 100 μm. The mechanical strength of the manufactured capsules was evaluated by the tube test method (internal impact method) In short, a weight of 100 g is dropped onto capsules (n=50) from a height of 8 cm and the number of broken capsules are counted and expressed as a percentage.

Capsules were stored at room temperature, at 2.5%, 10%, 23%, 33% and 45% relative humidity (RH) for 7 days. The measurements were done at room temperature.

Opacity Testing

Opacity was measured by a spectrophotometer (Color Eye XTH Portable Spectrophotometer) using the phase-contrast imaging method. For the measurement of light transmittance, the film samples were placed in the light pathway in the UV-VIS spectrophotometer, and the transmittance at 650 nm was recorded. Films were kept at room temperature.

For opacity testing, films of approximately about 100 μm thick were prepared from the different film-forming compositions as explained below. Such films correspond in terms of thickness to the side wall thickness of capsules ranging from 90-110 μm.

The term “opacity coefficient” as used herein corresponds to the Contrast Ratio Opacity (OP), i.e. the ratio between luminance or brightness measured against black and white background. OP measurements quantify how close to opaque a near-opaque material is.

The measurement is a two-part program metric where the Y (luminance or brightness) value is first measured on the sample backed by a black background, followed by a second measurement of the Y value of the sample backed by a white background. The resulting fraction is expressed as Y %, calculated as follows:

OP=Y _(black backing) /Y _(white backings)×100

Particles Size Measurement and Imaging

Particles size was determined using laser diffraction method (Mastersizer 2000, Malvern). The measurements were done on dry powder that was dispersed using the air pressure of 2 bar.

Particles were imaged with a scanning electron microscope (SEM).

High Shear Mixing

High shear mixing of the opacifying solution or dispersion was done using an Ultra Turrax T25 mixer (IKA) at a speed of 21000 rpm for at least 6 min. Concentration of the dispersion is at least 15 wt %, preferably above 20 wt %.

Example 1: Film-Forming Formulation Design

CaCO₃ was tested for its ability to induce opacity and for its effect on the mechanical strength of the polymeric films formed. This was tested on both cellulose-based (HPMC) and gelatin-based films.

A dispersion of non-encapsulated CaCO3 is first prepared and added to the film-forming formulation. The same general procedure is used for gelatin and HPMC formulations.

In short, 60 g of water was added to 22.45 g of precipitated CaCO₃ (PCC) and the mixture was homogenized with high shear mixing (e.g. high shear mixing at 21000 rpm (Ultra Turax) for 3×2 minutes with 30 sec pause between each mixing).

Subsequently a part of (e.g. 20 g) of the liquid film-forming HPMC or gelatin formulation, comprising 20.5 wt % HPMC in water or 31 wt % gelatin in water is added and mixed into the dispersion under stirring at 12000 rpm (e.g. Silverson apparatus), during e.g. 3 minutes, thereby forming a slurry. Said slurry is then mixed with the remaining part of the film-forming formulation, thereby forming the film-forming composition resulting in a 10 wt % CaCO₃ concentration based on the final dry weight of said film-forming composition.

Encapsulated CaCO₃ (10 wt % based on total dry weight of final capsule forming formulation) was dispersed in water by stirring with a helix mixer for about 45 minutes. The required quantity of the resulting dispersion was added to the liquid film-forming HPMC or gelatin formulation, comprising 20.5 wt % HPMC in water or 31 wt % gelatin in water based on total dry weight of final capsule forming formulation, and mixed.

HPMC-based films were prepared as follows: glass plates were kept at 60° C., the film-forming composition comprising the different amounts of CaCO₃ was kept at 28° C. and films were casted in a warm reservoir (40-50° C.) using e.g. a TLC plate coater, hand operated (CAMAG, Muttenz, CH). The films were then left to dry at 60° C. for about 1 hour and kept overnight at 22° C., at a RH of 50%.

Gelatin films were formed as follows: glass plates were kept at 60° C., the film-forming solution comprising the different amounts of CaCO₃ was kept at 55° C. and films were casted in a warm reservoir (about 60° C.) using e.g. a TLC plate coater (Camag C H). The films were then left to dry overnight at 22° C., at a RH of 50%.

The results of tests on HPMC and Gelatin (HGC) films are depicted in Table 1 below:

Reported particle Transmittance Mechanical Polymer Opacifier wt %* size (μm) Opacity (%) at 650 nm (%) properties HPMC TiO₂ 2.0 0.1-1   61.4 0.7 5 HPMC Precipitated CaCO₃ 10 0.7 32.8 7.9 3 (PCC) HPMC Encapsulated 10 3-5 37.05 9.3 1 agglomerated CaCO₃ HGC TiO2 2.0 0.1-1   61.4 0.7 5 HGC Precipitated CaCO₃ 10 0.7 23.88 27.5 3 (PCC) HGC Encapsulated 10 3-5 32.1 28.8 1 agglomerated CaCO₃ HGC Ground CaCO₃ 10 3.8 21.7 19.8 1 *based on dry weight of total final capsule forming formulation The score of 0 to 5 indicates the mechanical properties, 5 being the highest score, 0 being the lowest score in terms of mechanical properties. HPMC stands for hydroxypropylmethylcellulose HGC stands for hard gelatin capsule

The above results indicated that calcium carbonate shows potential as an opacifier retaining acceptable mechanical strength, although some differences were observed between CaCO₃ having different particle size. Particularly interesting is that the encapsulated and ground CaCO₃ result in less mechanical strength of the films.

In all further experiments, the term “precipitated CaCO₃” refers to PCC as indicated in Table 1.

Using scanning electron microscopy (SEM) imaging, the particle size and shape of the different CaCO₃ compositions were analysed. To this end, the particles were coated with metal and imaged using a scanning electron microscope known in the art. The scale bar is given in the images.

As follows from FIG. 1, the particle size and shape of the CaCO₃ compositions tested is quite different: FIG. 1 B shows agglomerated granules of the encapsulated CaCO₃, forming large particles (up to 100 μm), while FIG. 1 A shows much smaller particles of the precipitated CaCO₃ (PCC), having a small round/prismatic shape and being more uniform in particle shape and size distribution than the encapsulated CaCO₃.

Next, the particle size of the different CaCO₃ compositions was analyzed using a laser diffraction method as indicated above (cf. Table 2).

TABLE 2 Particle size and shape of precipitated and encapsulated CaCO₃ CaCO₃ D50 (μm) D4,3 (μm) SEM remarks precipitated CaCO₃ 0.91 6.19 Small, (PCC) round/prismatic, uniform particles encapsulated CaCO₃ 9.9 33.9 ~100 μm granules made of 1 μm particles

Example 2: Tests on HPMC Films and Capsules

Next a study was done on the impact of different levels of calcium carbonate on the films and capsules properties.

For this, the same procedure as used for producing HPMC films according to example 1 was used, but with several calcium carbonate concentrations and types (PCC as in Table 1 or 2, or encapsulated CaCO₃). The following protocol was used to prepare the 10 wt % CaCO₃ in a 20.5 wt. % HPMC-based films:

Step 1 HPMC solution HPMC 202.05 g Water 783.56 g (cc of HPMC 20.5 wt %) Step 2 Dispersion preparation CaCO₃ 22.45 g Water 60 g (cc of CaCO₃ (PCC) 27.2 wt %) Step 3 Slurry preparation Dispersion from Step 2 82.45 g HPMC solution from Step 1 20 g Step 4 Final formulation Polymer solution 965.61 g slurry 102.45 g Result 10 wt % CaCO₃ on 20.5 wt % HPMC capsule

In order to reach a film forming composition comprising 6.5 wt % of CaCO₃ based on the final dry weight of said film-forming composition, step 4 of the above protocol is as follows:

Step 1 HPMC solution HPMC 322.93 g Water 1252.36 g (cc of HPMC 20.5 wt %) Step 2 Dispersion preparation CaCO₃ 22.45 g Water 60 g (cc of CaCO₃ (PCC) 27.2 wt %) Step 3 Slurry preparation Dispersion from Step 2 82.45 g HPMC solution from Step 1 20 g Step 4 Final formulation Polymer solution 1555.29 g slurry 102.45 g Result 6.5 wt % CaCO₃ on 20.5 wt % HPMC capsule

In order to reach a film forming composition comprising 5 wt % or 7.5 wt % of CaCO₃ based on the final dry weight of said film-forming composition, the above protocols can be adjusted by changing the relative amount of HPMC film-forming formulation vs. CaCO₃ dispersion.

The opacity and light transmittance of the different HPMC-based films were tested and the results are presented in Table 3 below.

TABLE 3 opacity and transmittance at 650 nm of HPMC films containing different CaCO₃ types at two concentrations compared to transparent and films opacified with TiO2. 5% precip. 10% precip. 5% 10% CaCO₃ CaCO₃ Encapsulated Encapsulated Transparent 2% TiO2 (PCC) (PCC) CaCO₃ CaCO₃ Opacity (%) 15.09 63.09 23.3 32.8 25.07 37.05 Transmittance 90.1 0.7 26.6 7.9 27.3 9.3 at 650 nm (%)

Also the tensile properties of said films were tested using the Instron device according to ASTM D882-02. As shown in Table 4, the comparison between HPMC capsules comprising 5 or 10 wt % precipitated or encapsulated CaCO₃ does not show a marked difference in tensile properties because the HPMC films are by nature difficult to deform.

TABLE 4 Tensile properties of HPMC films with different CaCO₃ concentrations 5% precip. 10% precip. 5% 10% CaCO₃ CacO₃ Encapsulated Encapsulated Transparent 2% TiO2 (PCC) (PCC) CaCO₃ CaCO₃ 50% Young's 1800 (98) 1990 (95) 1862 (70) 1940 (80) 1803 (131.5) 1907 (158) RH modulus (MPa)(stdev) % 12.5 13.9 9.06 7.07 11 7.8 deformation (stdev) 3.3 2.9 1.16 1.1 2.9 1.5 Max % 18.8 20 11.73 9.8 14.7 11.12 deform. 23% Young 1852 (175) 2030 (132) 2081 (89.9) 2033 (113) 2056 (85.9) 2103 (137) RH modulus (MPa)(stdev) % 13.25 12.93 9.6 7.8 10.8 7.2 deformation (stdev) 3 2.6 1.95 1.8 2.9 1.1 max % 19.8 17.4 12.8 11.2 16.9 9.93 deform.

Next, HPMC capsules were formed using a conventional mold-dipping technique summarized in here: The dip pins of size 0 are pre-heated at about 73° C., while the dipping composition is maintained at 32° C. Capsules of size 0 are manufactured by the conventional dipping process, with pre-heated pins.

After the dipping, the capsules are dried with hot air at 60° C. and 40% RH for 30 minutes and then at about 22° C. and 50% RH, for about 20 minutes.

The influence of precipitated CaCO₃ and encapsulated CaCO₃ on mechanical strength when used at 10 wt % in HPMC capsules was compared and from the tube test evaluation it becomes clear that the precipitated CaCO₃ is better for mechanical performance (less broken capsules, cf. Table 5).

TABLE 5 comparison of effect of precipitated vs encapsulated CaCO₃ on mechanical strength of HPMC-based capsules: Total broken 10 wt % CaCO₃ % RH capsules (%) encapsulated CaCO₃ 10 100 23 88.24 33 47.06 45 0 precipitated CaCO₃ 10 96 (PCC) 23 46 33 10 45 0

The mechanical strength of HPMC-based capsules formed using a film-forming composition comprising 10 wt %, 7.5 wt % or 6.5 wt % precipitated CaCO₃ (prepared according to the protocols of Examples 1 and 2) was subsequently tested using the tube test (internal impact test) as Table 6: comparison of effect of different CaCO₃ concentrations on mechanical strength of HPMC-based capsules:

TABLE 6 comparison of effect of different CaCO₃ concentrations on mechanical strength of HPMC-based capsules: wt % Precipitated CaCO₃ Total broken (PCC) % RH capsules (%)  10% 10 96 23 46 33 10 45 0 7.5% 2.5 94 10 82 23 31 33 16 45 0 6.5% 2.5 90 10 68 23 18 33 6 45 2 5.5% 2.5 70 10 62 23 8 33 4 45 2

Based on said results, we can summarize the conditions for calcium carbonate to be effective in HPMC capsules into a concentration range of between 3 and 10 wt % of precipitated CaCO₃, which results in capsules with acceptable opacity and mechanical strength.

Example 3: Test on Gelatin Films

The film-forming composition and method from Example 1 was used to produce gelatin films.

Step 1 gelatin solution (HGC melt preparation) gelatin 322.94 g Water 718.79 g (cc of gelatin 31 wt %) Step 2 Dispersion preparation CaCO₃ 22.45 g Water 60 g (cc of CaCO₃ 27.2 wt %) Step 3 Slurry preparation Dispersion from Step 2 82.45 g gelatin solution from Step 1 20 g Step 4 Coloring the formulation Polymer solution 1021.71 slurry  102.45 Result 6.5 wt % CaCO₃ on 30.1 wt % gelatin capsule

Opacity and light transmittance at 650 nm were tested as explained above and the results are outlined in Table 7 below. Comparable results are obtained for precipitated CaCO₃ (PCC as in Table 1 or 2) and encapsulated CaCO₃.

TABLE 7 opacity and transmittance at 650 nm of gelatin-based films 5% 10% 5% 10% precip. precip. Encapsulated Encapsulated Transparent 2% TiO2 CaCO₃ CaCO₃ CaCO₃ CaCO₃ Opacity (%) 15.83 62.4 18.96 23.88 24.15 32.1 Transmittance at 82.2 1.7 49.2 27.5 48.5 28.8 650 nm (%)

Tensile tests on films were done as explained above for the HPMC films and show that films with precipitated CaCO₃ can be deformed more than films containing encapsulated CaCO₃ (cf. Table 8).

TABLE 8 Tensile properties of gelatin-based films with different CaCO₃ concentrations 5% 10% 5% 10% precip. precip. Encapsulated Encapsulated Transparent 2% TiO2 CaCO₃ CaCO₃ CaCO₃ CaCO₃ 50% Young's 2359 (123) 3032 (127) 2483 (145.5) 2507 (145.3) 2510.7 (91.2) 2600 (125) RH modulus (MPa)(stdev) % 24.5 12.44 15.9 13.3 11.8 11.5 deformation (stdev) 10.9 5 6.7 4.5 5 2.1 Max % def 47.3 27.28 30.4 21.4 24.6 15.1 23% Young 2398 (141) 3112 (122) 2784 (127) 2861 (126) 2521 (112.7) 2601 (151) RH modulus (MPa)(stdev) % 41.8 23 14.8 12.9 12.8 14.86 deformation (stdev) 11.2 9.4 5.9 6.3 5.8 6.1 max % def 58.6 44.44 27.4 28.8 28.6 27.4

This film-forming composition can also be used to produce gelatin-based capsules through conventional mold dipping. In short, by dipping stainless steel mold pins at room temperature (at about 22° C.) into a hot liquid gelatin solution (e.g. about 45° C.), a film of controlled dimensions is formed on the mold. After drying, this results in capsule halves with shell wall thickness of about 100 μm.

Example 4: Industrial Scale Test

Using the same film-forming composition as in Example 2, 550,000 HPMC capsules size 0 and 625,000 HPMC capsules size 1, were manufactured with a good quality and acceptable opacity. Overall trial outcomes are hence very positive. 

1. A capsule forming composition comprising: a film-forming agent, wherein the film-forming agent is gelatin, pullulan, cellulose based polymers or any combination thereof; and an opacifying agent in the form of precipitated calcium carbonate in an amount of between 4.5 and 6.5 wt % based on dry weight of the capsule forming formulation.
 2. The capsule forming composition according to claim 1, wherein said calcium carbonate has a substantially round or prismatic particle shape.
 3. The capsule forming composition according to claim 1, wherein said CaCO₃ has a median particle size of between 0.2 and 2.0 μm.
 4. The capsule forming composition according to claim 1, wherein said film-forming agent is a cellulose based polymer, wherein the cellulose based polymer is methylcellulose, hydroxymethylcellulose, hydroxypropylcellulose, methylhydroxyethylcellulose, hydroxypropylmethylcellulose, hydroxypropylmethylcellulose phthalate, hydroxypropylmethylcellulose acetate succinate, carboxymethylethylcellulose or a combination thereof.
 5. The capsule forming composition according to claim 1, wherein said film-forming agent is hydroxypropylmethylcellulose or gelatin.
 6. The capsule forming composition according to claim 1, wherein said film-forming agent is hydroxypropylmethylcellulose.
 7. The capsule forming composition according to claim 1, wherein said film-forming agent is gelatin.
 8. The capsule forming composition according to claim 1, wherein said film-forming agent is pullulan.
 9. The capsule forming composition according to claim 1, further comprising an additive comprising one or more of a gelling agent, gelling aid, viscosity modifier, de-foaming aid, plasticizer, lubricant, colorant, solvent, solvent aid, surfactant, dispersant, solubilizer, stabilizer, sweetener, adsorbent, adherent, antioxidant, antiseptic, preservative, desiccant, flavor, perfume, anti-oxidant, pH adjuster, binder, disintegrating agent, release-controlling agent.
 10. A capsule formed from the capsule forming composition according to claim
 1. 11. The capsule according to claim 10, which is a gelatin, pullulan or HPMC based capsule.
 12. A method of producing capsules with reduced light transmittance, comprising providing the film-forming composition according to claim 1, and forming capsules using a dip coating process.
 13. A method of preparing a film-forming composition according to claim 1, comprising the steps of: a) preparing an aqueous dispersion of precipitated calcium carbonate opacifier through mixing; b) preparing a film-forming formulation comprising one or more film-forming agents, wherein the film-forming agent is gelatin, pullulan, cellulose based polymers or any combination thereof; c) adding the aqueous dispersion of step a) to the solution of step b); and d) mixing the resulting dispersion of step c), thereby obtaining the film-forming composition, wherein the film-forming composition comprises between 4.5 and 6.5 wt % precipitated calcium carbonate based on final dry weight of the film-forming composition.
 14. The method according to claim 13, wherein step c) is performed in two steps: c1) adding a part of the film-forming formulation of step b) to the dispersion of step a) to form a slurry and c2), adding said slurry to the remaining film forming formulation.
 15. The method according to claim 13, wherein the film-forming agent comprises gelatin, pullulan, HPMCAS or HPMC.
 16. The method according to claim 15, wherein the film-forming agent comprises gelatin or HPMC.
 17. The method according to claim 15, wherein the film-forming agent comprises gelatin.
 18. The method according to claim 15, wherein the film-forming agent comprises HPMC.
 19. A method of making capsules comprising the steps of: a) preparing a film-forming composition according to the method of claim 13 and b) producing a capsule by means of dip molding.
 20. A capsule forming composition comprising: a film-forming agent selected from the group consisting of: gelatin, pullulan, or cellulose based polymers; and an opacifying agent in the form of precipitated calcium carbonate in an amount of between 4.5 and 6.5 wt % based on dry weight of the capsule forming formulation. 